    Metal Additive Manufacturing Conference 2018

    21–23 Nov 2018
    Wirtschaftskammer Österreich
    Europe/Vienna timezone
    Registration is closed!

    Support

    Session

    Related Processes (I)

    21 Nov 2018, 17:20
    Julius Raab Saal (Wirtschaftskammer Österreich)

    Julius Raab Saal

    Wirtschaftskammer Österreich

    Wiedner Hauptstraße 63 1045 Vienna, Austria

    Conveners

    Related Processes (I)

    • Harald Bleier (ecoplus. Niederösterreichs Wirtschaftsagentur GmbH)

    Presentation materials

    There are no materials yet.

    1. 5. LITHOGRAPHY-BASED ADDITIVE MANUFACTURING OF FUNCTIONAL METAL COMPONENTS
      Dr Gerald Mitteramskogler (Lithoz GmbH)
      21/11/2018, 17:20
      Related Processes
      Oral Presentation
      Lithographic additive manufacturing (AM) technologies are based on the concept of photopolymerization and are known for their process inherent high precision and good surface quality compared to other AM techniques. In this work, metallic suspensions comprising a photoreactive binder and 316L powder (50vol%) were used as starting material. After printing, the obtained green parts undergo a...
      Go to contribution page
    2. 71. 3D PRINTING OF «ALUMINUM - 10 -20 WT. % ALUMINA» COMPOSITES WITH CORE-SHELL PARTICLES AS RAW MATERIALS
      Mr Alexey Arnautov (National University of Science and Technology "MISiS")
      21/11/2018, 17:40
      Related Processes
      Oral Presentation
      The work is devoted to the advanced 3D printing of “aluminum-10-20 wt. % alumina” composite with core-shell structure. The process of core-shell “aluminum-10-20 wt. % alumina” composite preparation was based on the aluminum powders selective oxidation in water and following drying at 120 °C and calcination of the obtained “aluminum-10-20 wt. % alumina” composite at 600 °C. The process of...
      Go to contribution page
    Building timetable...